주식회사 에이피아이티

Introduction

Mission

Incorporation Mission and Vision

Mission

Realization of Carbon Zero Society by Aerogel-based Energy Save

Vision

Innovative Energy Save & Global Platform Company in Environmental Materials Field

Core Value

Technology Ultra-high Efficiency and Ultra- lightweight

Inside the Organization Communication and Creativity

Outside the Organization Energy Save and Eco-friendly Society

High performance of Core Technology

Creative Thinking by Communication

High Efficiency of Production Process

Constant Development of Eco-friendly Product

Product characteristic (TDS)
Properties		Aerogel⁺
Thermal characteristics	Available temperature (℃)	-50 ~ 500
Thermal characteristics	Thermal conductivity (W/m·K)	0.02-0.03
Pore characteristics	Specific surface area (m²/g)	Over 900
	Pore volume (cc/g)	2.38
	Pore size (nm)	6.98
	Porosity (%)	98
Other characteristics	Average particle size (μm²)	3.06
	Apparent density (g/cc)	Around 0.06
	Contact angle (°)	144

제품특성 (TDS)
물성		Aerogel⁺
열적 특성	가용온도 (℃)	-50 ~ 500
열적 특성	열전도도 (W/m·K)	0.02-0.03
내부 기공 특성	비표면적 (m²/g)	900 이상
	기공 부피 (cc/g)	2.38
	기공 크기 (nm)	6.98
	기공률 (%)	98
기타 특성	평균 입자 크기 (μm²)	3.06
	겉보기 밀도 (g/cc)	약 0.06
	접촉각 (°)	144

Product characteristic (TDS)
Binder type	aqueous acrylic system
Color	white
Package	4L / 18L
Density	0.5 ~ 0.6 g/ml
Viscosity	940 cps
Method	Blush, spray
Coating area	0.2 ~ 0.3 m²/L
Volume solid	59.2%
Coating thickness	0.5 ~ 2 mm (one time)
Re-paint time	4h (25℃)
Drying time	6h (25℃)
Storage	2 months
Thermal conductivity	< 0.040 W/m∙K (at 10 mm)
Available temperature	<200℃< /td>

제품특성 (TDS)
페인트 종류	수성 아크릴계
색상	백색
포장	4L / 18L
비중	0.5 ~ 0.6 g/ml
점도	940 cps
도장방법	브러쉬, 헤라, 스프레이
이론도포면적	0.2 ~ 0.3 m²/L
부피고형분	59.2%
추천도막두께	0.5 ~ 2 mm (1회)
재도장시간	4시간 (25℃)
건조시간	6시간 (25℃)
저장 및 보관	2개월
열전도도	< 0.040 W/m∙K (at 10 mm)
사용온도	<200℃< /td>

Product characteristic (TDS)
Binder type	Modified Silicates
Color	White
Package	4L / 18L
Density	0.5 ~ 0.7 g/ml
Viscosity	1,020 ~ 1,310 cps
Method	Blush, spray
Coating area	0.2 ~ 0.3 m²/L
Volume solid	68.30%
Coating thickness	0.5 ~ 2 mm (one time)
Thermal conductivity	0.05
Available temperature	> 500℃

제품특성 (TDS)
페인트 종류	변성 실리케이트계
색상	백색
포장	4L / 18L
비중	0.5 ~ 0.7 g/ml
점도	1,020 ~ 1,310 cps
도장방법	스프레이, 브러쉬, 헤라
이론도포면적	0.2 ~ 0.3 m²/L
부피고형분	68.30%
추천도막두께	0.5 ~ 2 mm (1회)
열전도도	0.05
사용온도	> 500℃

Product characteristic (TDS)
Major material	Acryl copolymer
Color	White
Package (area)	10 cm ~ 50 cm
Package (thickness)	0.5 ~ 2.5 T
Density	0.5 ~ 0.6 g/ml
Method	Glue or tape
Thermal conductivity	< 0.045 W/m∙K (at 10 mm)
Available temperature	<200℃< /td>

제품특성 (TDS)
모재 종류	아크릴 공중합체
색상	백색
포장 (면적)	10 cm ~ 50 cm
포장 (두께)	0.5 ~ 2.5 T
밀도	0.5 ~ 0.6 g/ml
부착방법	접착제 또는 양면테이프
열전도도	< 0.045 W/m∙K (at 10 mm)
사용온도	<200℃< /td>

Product characteristic (TDS)
Major material	Acryl copolymer
Color	White
Package (area)	10 cm ~ 50 cm
Package (thickness)	0.5 ~ 1 T
Density	0.5 ~ 0.6 g/ml
Method	Remove the film
Thermal conductivity	0.035 ~ 0.037 W/m-k
Available temperature	120℃ or less

제품특성 (TDS)
모재 종류	아크릴 공중합체
색상	백색
포장 (면적)	10 cm ~ 50 cm
포장 (두께)	0.5 ~ 1 T
밀도	0.5 ~ 0.6 g/ml
부착방법	필름 제거 후 부착
열전도도	0.035 ~ 0.037W/m-k
사용온도	120℃ 이하

Product characteristic (TDS)
Matrix and filler material	Ceramic fiber blanket+ Silica·Zirconia·Alumina·Titania based aerogel
color	White
Package (thickness)	10 T
Compressive strength	15-25 MPa
Density	< 0.12 g/ml
Contraction rate	Under 1%
Thermal conductivity	< 0.025 W/m∙K (at 10 mm)
Available temperature	>700℃

제품특성 (TDS)
모재 및 충진재 종류	세라믹 섬유+실리카·지르코니아·알루미나·타이타니아 에어로겔
색상	백색
포장 (두께)	10 T
압축강도	15-25 MPa
밀도	< 0.12 g/ml
수축률	1% 이하
열전도도	< 0.025 W/m∙K (at 10 mm)
사용온도	700℃ 이상